Effect of elastomeric urethane monomer on physicochemical properties and shrinkage stress of resin composites

Abstract This study aimed to evaluate the effect of an elastomeric urethane monomer (Exothane-24) in different concentrations on physicochemical properties, gap formation, and polymerization shrinkage stress of experimental resin composites. All experimental composites were prepared with 50 wt.% of Bis-GMA and 50 wt.% of TEGDMA, to which 0 wt.% (control), 10 wt.%, 20 wt.%, 30 wt.%, and 40 wt.% of Exothane-24 were added. Filler particles (65 wt.%) were then added to these resin matrixes. Ultimate tensile strength (UTS: n = 10), flexural strength (FS: n = 10), flexural modulus (FM: n = 10), hardness (H: n = 10), hardness reduction (HR: n = 10), degree of conversion (DC: n = 5), gap width (GW: n = 10), and polymerization shrinkage stress in Class I (SS-I: n = 10) and Class II (SS-II: n = 10) simulated configuration. All test data were analyzed using one-way ANOVA and Tukey's test (α = 0.05; β= 0.2). Exothane-24 in all concentrations decreased the H, HR, DC, GW, SS-I, and SS-II (p < 0.05) without affecting the UTS, and FS (p > 0.05). Reduction in FM was observed only in the Exothane 40% and 30% groups compared to the control (p < 0.05). Exothane-24 at concentrations 20% and 30% seems suitable since it reduced GW and polymerization SS without affecting the properties of the composite resins tested, except for H.

Resumo Este estudo teve como objetivo avaliar o efeito de um monômero elastomérico de uretano (Exothane-24) em diferentes concentrações em propriedades físico-químicas, formação de fenda e tensão de contração de polimerização de resinas compostas experimentais. Todos os compósitos experimentais foram preparados com 50% em peso de Bis-GMA e 50% em peso de TEGDMA, nos quais 0% (controle), 10%, 20%, 30% e 40% em peso de Exothane-24 foram adicionados. Partículas de carga (65% em peso) foram então adicionadas as matrizes resinosas. Resistência coesiva (RC: n = 10), resistência à flexão (RF: n = 10), módulo de flexão (MF: n = 10), dureza (D: n = 10), redução de dureza (RD: n = 10), grau de conversão (GC: n = 5), largura de fenda (LF: n = 10) e tensão de contração de polimerização em simulações de cavidades Classe I (TC-I: n = 10) e Classe II (TC-II: n = 10). Todos os dados do teste foram analisados usando one-way ANOVA e teste de Tukey (α = 0,05; β = 0,2). O Exothane-24 em todas as concentrações diminuiu a D, RD, GC, LF, TC-I e TC-II (p < 0,05) sem afetar o RC e RF (p > 0,05). A redução da MF foi observada apenas nos grupos Exothane 40% e 30% em relação ao controle (p < 0,05). O Exothane-24 nas concentrações de 20% e 30% pareceu ser adequado, pois reduziu LF e TC de polimerização sem afetar as propriedades das resinas compostas testadas, exceto para D.

Posterior rehabilitation using 3D-printed dental implants and synthetic regenerative biomaterials / Reabilitação posterior com implantes impressos e biomateriais sintéticos

Aim: To describe through a clinical case report the surgical sequence of rehabilitation with 3D-printed implants associated with maxillary sinus floor lift with synthetic regenerative materials, including biphasic bioceramic. Case Report: Patient had an agenesis of the upper left premolars (#12 and #13), a vertical bone deficiency caused by maxillary sinus' pneumatization, and a horizontal alveolar resorption around the missing teeth area. During the surgical procedures, incisions, detachment, and osteotomy were performed in the lateral region of the maxillary sinus. The sinus membrane was detached and lifted 10 mm. Then, a thick poly(dioxanone)-based synthetic resorbable membrane (Plenum) was inserted and adapted inside the sinus to protect the sinus membrane. After the osteotomies with sub-instrumentation, 3D-printed implants (Plenum) were installed in the #12 area (3.5mm x 11.5 mm; 30N) and #13 area (4.0mm x 10mm; 20N). The maxillary sinus was entirely filled with a biphasic bioceramic, HA/ß-TCP (70:30) 500-1000 µm (Plenum) and covered by the same synthetic resorbable membrane. Connective tissue graft from the palatal area was positioned internally to the flap and stabilized with sutures to improve the vestibular tissue architecture. The entire surgical wound was sutured, and the tissues stabilized. No complications occurred in the postoperative period. Conclusion: The use of synthetic regenerative memberane and 3D-printed implants seems to be a promising option in areas of deficient bone remnants (AU)

Objetivo: Descrever por meio de um relato de caso clínico a sequência cirúrgica de reabilitação com implantes obtidos por impressão 3D associados à elevação do assoalho do seio maxilar com materiais regenerativos sintéticos, incluindo uma biocerâmica bifásica. Relato de Caso: Paciente apresentava agenesia dos pré-molares superiores esquerdos (24 e 25), deficiência óssea vertical causada pela pneumatização do seio maxilar e reabsorção alveolar horizontal ao redor da área dos dentes ausentes. Durante os procedimentos cirúrgicos foram realizados incisões, descolamento e osteotomia na região lateral do seio maxilar. A membrana sinusal foi descolada e elevada 10 mm. Em seguida, uma membrana reabsorvível sintética à base de poli(dioxanona) espessa (Plenum) foi inserida e adaptada dentro do seio para proteger a membrana do seio. Após as osteotomias com subinstrumentação, implantes impressos em 3D (Plenum) foram instalados na área do 24 (3,5mm x 11,5mm; 30N) e na área do 25 (4,0mm x 10mm; 20N). O seio maxilar foi inteiramente preenchido com biocerâmica bifásica, HA/ß-TCP (70:30)500-1000 µm (Plenum) e recoberto pela mesma membrana sintética reabsorvível. O tecido conjuntivo da região palatina foi posicionado internamente ao retalho e estabilizado com suturas para melhorar a arquitetura do tecido vestibular. Toda a ferida cirúrgica foi suturada e os tecidos estabilizados. Não ocorreram complicações no pós-operatório. Conclusão:A utilização de biomateriais regenerativos sintéticos e implantes impressos parece ser uma opção promissora em áreas de remanescentes ósseos deficientes.(AU)

Effect of light attenuation through veneers on bond strength of adhesives with photoinitiator combinations

Abstract This study aimed to evaluate the effect of light attenuation through ceramic veneers and resin cement on degree of conversion (DC), cohesive strength (CS), and microshear bond strength (μSBS) of experimental adhesive systems. Experimental etch-and-rinse and self-etch adhesives were combined with different ratios of camphorquinone (CQ) and diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) photoinitiators: CQ-only; 3CQ:1TPO; 1CQ:1TPO; 1CQ:3TPO and TPO-only. Square-shaped ceramic veneer (IPS Empress Esthetic, Ivoclar Vivadent) (n = 10; 10mm long x 10mm wide x 0.5mm thick) and resin cement specimens (Variolink Esthetic LC, Ivoclar Vivadent) (n = 10; 10 mm long x 10 mm wide and 0.3 mm thick) were prepared. Light transmittance of a multiple-peak LED (Bluephase G2, Ivoclar Vivadent) was measured through restorative materials using a spectrometer (n = 5). Adhesive specimens were analyzed for DC, CS, and μSBS by light-curing the adhesive with or without (control) ceramic veneer, and with resin cement fixed to output region of the light-curing tip (n = 10). Data were submitted to ANOVA and Tukey's test (α = 0.05). Total light transmittance through the restorative materials was attenuated, and this attenuation was more evident for the violet spectrum. The DC for the TPO groups in ratios up to 1CQ:1TPO was similar to the control. 1CQ:3TPO showed lower values for CS. μSBS was reduced for all groups with light attenuation, but lower values were observed for 1CQ:3TPO and TPO-only. In conclusion, light transmission was reduced with interposed restorative materials. Adhesives combined with CQ and TPO up to 1CQ:1TPO showed greater cure efficiency and mechanical properties compared with a higher amount of TPO.

Effect of combining photoinitiators on cure efficiency of dental resin-based composites

Abstract Camphorquinone is the most conventionally used photoinitiator in Dentistry. Although different alternative photoinitiators have been proposed, no photoinitiator was capable of completely substituting camphorquinone. The combination of photoinitiators has been considered the best alternative. Objectives: To evaluate the effect of combining Norrish type I and II photoinitiators on the cure efficiency of dental resin-based composites. Methodology: Experimental composites were produced containing different photoinitiator systems: Norrish type I-only, mono-alkyl phosphine oxide (TPO); Norrish type II-only, camphorquinone (CQ); or its combination, CQ and TPO, in a 1: 1 molar ratio. UV-vis absorption spectrophotometry was performed to assess the consumption of each photoinitiator after curing (n=3). A multi-wave LED (Bluephase® G2, Ivoclar Vivadent) was pre-characterized and used with a radiant exposure of 24 J/cm2. The degree of conversion was evaluated by Raman spectrometry, and the elution of the monomers by nuclear magnetic resonance analysis (n=3). Data were analyzed using ANOVA and Tukey's test (α=0.05; β=0.2). Results: The combination of CQ and TPO increased the consumption of the photoinitiator system compared to CQ-only (p=0.001), but presented similar consumption compared to TPO-only (p=0.52). There was no significant difference in the degree of conversion between the composites regardless of the photoinitiator system (p=0.81). However, the elution of the monomers was reduced when both photoinitiators were combined. TPO-based material presented the highest elution of monomers. Conclusions: The combination of the photoinitiator systems seems to be beneficial for the cure efficiency of dental resin-based composites.

The effect of shade and curing mode on cure efficiency of dual-cure resin cements / Efeito da cor e do modo de cura na eficiência de cura de cimentos resinosos de cura dual

Objective: To evaluate the effect of shade and curing mode on cure efficiency of two dual-cure resin cements. Material and Methods: Two shades (A2 and TRANS) of two different dual-cure resin cements (G-CEM, GC Dental and SET PP, SDI) were submitted to different curing modes: light curing through a 2 mm thick ceramic disc (IPS Empress Esthetic, A2, Ivoclar Vivadent) for 20 s (16 J/cm2), 40 s (32 J/ cm2) or 80 s (64 J/cm2) performed immediately or with 1 or 5 min of delay. Fourier transform infrared spectroscopy (FT-IR) was used to evaluate the degree of conversion (DC) after 48 h. For the statistical analysis, data were submitted to threeway analysis of variance, followed by Tukey’s test for multiple comparisons (p<0.05). Results: Shade influenced DC (%) for the dual-cure resin cements tested (p=0.00001). TRANS shade showed lower DC (%) for both cements when there was no delay before light-curing (p=0.00001). Curing mode also influenced DC (%) for the dual-cure resin cements tested: radiant exposure greater than 32 J/cm2 and delaying light-curing for 1 to 5 min increased the DC (%) for both dual-cure resin cements evaluated. Conclusions: One minute delay prior to light-curing improved the cure efficiency and may be a more clinically acceptable approach to increase the degree of conversion of dual-cure resin cements.

Objetivo: Avaliar a influência da cor e do modo de polimerização no grau de conversão de dois cimentos resinosos duais. Material e Métodos: Duas cores (A2 e TRANS) de dois cimentos resinosos duais (G-CEM, GC Dental e SET PP, SDI) foram submetidos a diferentes modos de cura: fotoativação através de um disco de cerâmica de 2 mm de espessura (IPS Empress Esthetic, A2, Ivoclar Vivadent) por 20 s (16 J/cm2), 40 s (32 J/cm2) ou 80 s (64 J/cm2) realizada imediatamente ou após 1 ou 5 min de espera. Espectrometria com transformada de Fourier (FT-IR) foi utilizada para avaliação do grau de conversão (GC) após 48 h. Para a análise estatística, os dados foram submetidos à análise de variância com três fatores, seguida de teste de Tukey para comparações múltiplas (p=0.05). Resultados: A cor influenciou o GC (%) dos cimentos resinosos duais avaliados (p=0.00001). A cor TRANS resultou menor GC (%) para ambos os cimentos quando não houve espera antes da fotoativação (p=0.00001). O modo de cura também teve influência n o GC (%) dos cimentos resinosos duais avaliados: doses de energia superiores a 32 J/cm2 e espera de 1 ou 5 min antes da fotoativação aumentou o GC (%) dos dois cimentos resinosos duais avaliados. Conclusão: Um min de espera antes da fotoativação melhorou a eficiência de cura e pode ser uma abordagem clinicamente aceitável para aumentar o grau de conversão de cimentos resinosos duais.